Complete cleaning set
Complete cleaning set holder, magnetic, with 3 cans of 400 ml each *Sucor Protect,G10, temporary anti-corrosion agent for injection molds for corroding steel molds *SuCor Uni, universal care oil, reliably prevents rusting, penetrates moisture, very good sliding properties, silicone-free, *DiviD Uni, mold release agent, silicone-free
€24.00
*
DIN 1530 form A
Copper core pin
Material: special copper alloys (beryllium alloy) Material features: highest thermal conductivity approximately 10 times higher than tool steel, corrosion-resistant, softening temperature: 420 ° C Hardness: Shaft: HB 185-210 The pins can be smoothly rotated to any desired degree and any form, milled or ground. Surface of copper core pins can be coated. Please ask us
From €27.47
*
DIN 1530 form A blank
Ejector pin nitrided
nitrided, blank, with cylindrical head|material: 1.2343 or 1.2344, start resistance min.600°C. shaft hardness: surface bad- or gas nitrided, min. 950 HV. core strength min. 1400 N/mm2. |polished surface after nitriding. head hardness: 50 ± 5 HRC
From €3.01
*
DIN 1530 form A black
Ejector pin
nitrided, black, with cylindrical head|material: 1.2343 or 1.2344, start resistance min.600°C. |shaft hardness: surface plasma-nitrided, black oxidized, min. 950 HV. core strength min. 1400 N/mm2.|head hardness: 50 ± 5 HRC
From €3.09
*
DIN 1530 form A unnitrided
Core pin
material 1.2343 oder 1.2344, pre-toughened|head hardness ca. 40 - 45 HRC, blank 50 ± 5 HRC
From €3.66
*
DIN 1530 form AH
Ejector pin
hardened, with cylindrical head material: 1.2210 or 1.2067 or similar, start resistance min.200°C. shaft hardness 60 ±2 HRC, head hardness 45 ± 5 HRC.
From €1.75
*
DIN 1530 form AH-HSS
Ejector pin
material: HSS-1.3343 shaft hardness 60 ±1 HRC head hardness 42± 2 HRC These ejector Pins of HSS are heat resistant up to 560 ° C. increase the wear the pins can be nitrided and TIN or TiCN, etc. coated.
From €4.10
*
DIN 1530 form AH-corrosion resistant
Ejector pin
hardened, with cylindrical head| material: 1.4125| shaft hardness 58 + 4 HRC, head hardness 30 +10 HRC| Especially suitable for the medical and food industries|
From €5.07
*
DIN 1530 form C
Ejector pin
nitrided, with cylindrical head|material: 1.2343 or 1.2344, start resistance min.600°C.| shaft hardness: surface bath- or gas-nitrided, min 950 HV.|core strenght min. 1400 N/mm2.| head hardness: 50 ± 5 HRC.
From €8.17
*
DIN 1530 form CH
Ejector pin
hardened, with cylindrical head material: 1.2210 or 1.2067 or similar, start resistance min.200°C. shaft hardness 60 ±2 HRC, head hardness 45 ± 5 HRC.
From €6.71
*
DIN 1530 form D
Ejector pin
hardened, with conical head material: 1.2210/1.2067 or similar, start resistance min.200°C. shaft hardness 60 ±2 HRC, head hardness 45 ± 5 HRC.
From €1.70
*